Polyester webbing with broken edges cannot continue to be used, because when the industrial flat webbing is under load, if there is a break on the edge of the webbing, when it is under stress, the industrial yarn will be disconnected at the break and cannot bear the force. And the first to tear, resulting in accidental losses, so when using polypropylene webbing to bind or fasten objects, you should first check whether the two ends of the white webbing are damaged, even if it is only worn, you need to pay attention.

When the polypropylene fiber webbing is woven, the number of radial threads arranged at both ends is larger than that of the middle part, because the strength of the two ends will be larger when the 50mm webbing bears the force, so if the fiber threads placed in the diameter holes are When the number is the same as the number of the middle part, its bearing capacity will not meet the requirements of use, and the phenomenon of tearing the woven bag will occur under a certain strength.
Therefore, if the edge friction damage is found before the use of the industrial webbing, it should be tested for tension before use, or the damaged webbing can be used for decoration, and the rash use will only cause accidents. The use of synthetic fiber webbing is from understanding Its usage and precautions begin to avoid losses due to lack of information.